If that's the case, I wonder why they would *want* to dispense / recommend
a 50/50 mix.

I'm not saying you're wrong, I'm just saying it's strange. Is there some
common application where rubbery epoxy would be desired?

Regards,

-Jeff

On Aug 1, 8:28am, Andy Carlson wrote:
Subject: Re: [STMFC] Devcon Epoxy (was Using CA as a gap filler)
Rob, the epoxy will always be rubbery.
-Andy Carlson

--- Rob Kirkham <rdkirkham@shaw.ca> wrote:

... have one
question for clarification:
the 50/50 mix that leads to rubbery panels - I take
it that is short term
and the stuff hardens out over time?????? Otherwise
I can't see much use
for the rubbery mix even for wavy panels.
--
Jeff Aley jaley@pcocd2.intel.com
DPG Chipsets Product Engineering
Intel Corporation, Folsom, CA
(916) 356-3533